Plaster line mold silicone

    Plaster line mold silica gel is a special turning material for the production of plaster line building materials. It has good fluidity simple operation. The two components are mixed according to the proportion of the proportion the bubbles can be filled brushed. use.
  • Product description

Introduction of Plaster Line Mold Silicone:

Generally, the plaster line mold silica gel used by customers to make silicone molds is mostly condensation mold silica gel. A few customers like to use addition mold silica gel. Plaster line mold silica gel is divided into AB two components, A component silica gel,  B component curing agent. After mixing the silicone  curing agent, it can be formed.


Uses of plaster line mold silicone:

Plaster line mold silica gel is suitable for all kinds of large, medium  small pieces of plaster crafts, plaster decorative building materials, copying of building decoration technology  the production of silicone molds. The recommended hardness range is 15-35 Shore degrees,  the final hardness value is determined according to customer product requirements  processes.

 

Features of plaster line mold silicone:

1. Good fluidity, easy operation, easy demoulding;


2. The mould made is  deformed  has the advantages of high temperature resistance, corrosion resistance, acid  alkali resistance;


3. High tear strength, good tensile force, the mold can be reused,  the number of mold reversals is large;


4. Low shrinkage rate (≤0.3%), fast curing  forming at room temperature, performance can be adjusted according to customer requirements.


 

Plaster line mold silicone operation:

1. Prepare tools: knives, rulers, brushes, scissors, wooden boards, etc.;


2. Deal with the mold species, fix the mold species on the wooden board with sludge, smooth the sludge by hand with water,  cut off the excess sludge around;


3. According to the product structure, pattern  purpose, the silica gel is weighed  proportioned,  the proportion between silica gel  curing agent is 100:2-2.5;


4. Stir the proportioned silica gel evenly  put it into the vacuum machine to vacuum (pump the vacuum to -0.1mpa, so as to prevent the mold   bubbles  affect the quality. If there is no vacuum machine, the curing agent can be reduced Add ratio to extend the curing time  release excess bubbles);


5. Apply the vacuumed silica gel evenly to the mold (generally, you can brush the second layer in about 15 minutes, with the silica gel required for the second layer,  repeat the first layer of silica gel 2-3 times);


6. When the silica gel is  flowing, stick a layer of gauze on the silica gel. The advantage of this is that it can enhance the strength  tear resistance of the silica gel,  then apply a layer of silica gel evenly (add a layer of gauze according to the size of the product. Generally no more than two floors);


7. After the silica gel is applied, lay a tenon on the edge  close the mold with the outer mold to make the mold good;


8. After the silica gel is cured, the outer mold can be made, the shape of the outer mold is fixed with a wooden board, the adjusted plaster is poured into the mold,  the plaster is smeared flat;


9. After the outer mold is completely cured, remove the board, remove the entire outer mold  the silicone mold, check the silicone mold, trim the silicone mold with scissors,  trim the plaster outer mold;


10. After the production of the silicone mold is completed, it can generally be put into production after 24 hours.


 石膏线模具硅胶操作


Note on operation of plaster line mold silica gel:

1. Use clean operating tools to prevent silica gel  mixing with impurities  affecting curing;


2. The amount of curing agent added should depend on the temperature,  it will decrease if the temperature is higher. Excessive addition of curing agent will affect the quality of the mold,  the silicone mold will become brittle; adding less curing agent will prolong the curing time;


3. Vacuum to -0.1mpa is enough,  the vacuum time should  be too long to prevent cross-linking reaction of silica gel when vacuuming, causing silica gel to become piece by piece, causing waste of raw materials;


4. After making the silicone mold, store it in a ventilated, cool  dry place,  put it into production after 24 hours.


 

Plaster line mold silicone parameters:

color

White/Translucent

Hardness 

(Shore A)

15±2

20±2

25±2

30±2

33±2

40±2

Vulcanizing agent addition (%)

2-3

Dynamic viscosity (mPa.s)

1.3w±0.2w

1.7w±0.2w

2.5w±0.2w

2.7w±0.2w

2.5w±0.2w

1.5w±0.2w

Tensile strength (MPa)

2.5

2.8

3.4

4.0

3.5

Tearing strength (KN/m)

16±2

19±2

24±2

25±2

21±2

Elongation(%)

380

530

410

420

450

180

Density (g/cm³)

1.08

1.09

Operating time (min)

30-50

30-40

30-50

Curing time (h)

4-5

3-4

4-5

Linear shrinkage rate (%)

0.3

standard packaging

25kg

Note: The above parameters are only regular parameters. If you have special requirements, please contact our company; the hardness, viscosity,  operating time after curing can be specially adjusted  provided according to customer needs.


label

Contact information

液体硅胶,食品硅橡胶,人体硅橡胶厂家 Contact: Manager Zhang 13823551369

                   Manager Chen 13316540440

液体硅胶,食品硅橡胶,人体硅橡胶厂家 Mail box: 3265465343@qq.com

液体硅胶,食品硅橡胶,人体硅橡胶厂家 Fax: 0755-84826339

液体硅胶,食品硅橡胶,人体硅橡胶厂家 Address: 3020, Longcheng Avenue, Longgang District, Shenzhen, Guangdong Province


宏图手机站
宏图阿里店铺
Hongtu Mobile Station
Ali shop